Selective Laser Melting DMLS/SLM/PBF
The professional 3D printing technology of metal laser melting – DMLS / SLM/PBF – allows to build a part in a definitve metallic material.
A 3D printed metallic part has a behaviour and mechanical properties identical to the same part obtained in a traditional way, by CNC machining or casting.
The 3D printed parts could be then post-process by heat treatment , surface treatment or machining.
Minimum buildable thickness:0,8mm
Average surface roughness:5/6 µm
Accuracy (part dimension ≤ 150mm):±0,3mm
Accuracy (part dimension > 150mm):±0,3mm
Aluminum AlSi10Mg
One of the most used alloy in casting; suggested material in any application where the weight reduction is a must, but with always good mechanical behaviour. Good Thermal properties and wealdability completes the material features.
Mechanical Properties | |
---|---|
Maximum dimensions | 250mm x 250mm x 280mm |
Tensile strength | 405MPa |
Yield Strength (Rp 0.2%) | 230MPa |
Elongation at Break | 4% |
Young’s modulus | 70000 MPa |
Hardness | 120 HBW |
Aluminum AlSi7Mg0.6
One of the most used alloy in casting; suggested material in any application where the weight reduction is a must, but with always good mechanical behaviour. Good Thermal properties and wealdability completes the material features. The main difference respect to AlSi10Mg is that this alloy is Aerospace certified (A357) and shows a better machinability on CNC machines
Mechanical Properties | |
---|---|
Maximum dimensions | 500mm x 280mm x 350mm |
Tensile strength | 390 MPa |
Yield Strength (Rp 0.2%) | 220 MPa |
Elongation at Break | 6 % |
Young’s modulus | 68000 MPa |
Hardness | 110 HBW |
Stainless Steel AISI 316L
Steel with good corrosion resistance. The stainless steel AISI 316L, with low carbon content is perfect for medical and food application.The material is also suitable for cnc machining and polishing processes.
Mechanical Properties | |
---|---|
Maximum dimensions | 250mm x 250mm x 280mm |
Tensile strength | 550 MPa |
Yield Strength (Rp 0.2%) | 450 MPa |
Elongation at Break | 40% |
Young’s modulus | 160000 MPa |
Hardness | 20 HRC |
Titanium Ti6Al4V
One of the most performing alloy in metal additive manufacturing; it shows excellent corrosion resistance, also to high temperture. Ideal solution for component with thin wall and for medical application, thanks to its biocompatibility. In the Grade 23 ELI form contains low oxygen percentage.
Mechanical Properties | |
---|---|
Maximum dimensions | 250mm x 250mm x 280mm |
Tensile strength | 1150 MPa |
Yield Strength (Rp 0.2%) | 1050 MPa |
Elongation at Break | 6% |
Young’s modulus | 110000 MPa |
Hardness | 34 HRC |

Selective Laser Sintering -SLS- Materials
The professional 3D printing technology of Selectivel Laser Sintering – SLS – allows to build plastic parts with an high level of finiture and performance.
The SLS 3D printer machines use an high power laser to melt, layer by layer, the plastic powders present in the build chamber.
The obtained pieces are excellent concerning both the mechanical properties and the finiture quality
Minimum buildable thickness:1mm
Average surface roughness:5/6 µm
Accuracy (part dimension ≤ 150mm):±0,3mm
Accuracy (part dimension > 150mm):±0,05mm ogni 25mm
PA12 C.F.
Nylon 12 carbon fiber loaded; it’s an extremely resistant plastic material with low density, ideal for structural and weigth reduction application.
Mechanical Properties | |
---|---|
Maximum dimensions | 380mm x 330mm x 300mm |
Ultimate Tensile Strenght | 85 MPa |
Tensile Modulus | 7900 MPa |
Flexural Modulus | 9000 MPa |
Elongation at Break | 4% |
Heat Deflection Temperature | 175° |
Density | 1,1 gr/cm3 |
PA12 G.F.
Nylon 12 glass fiber loaded; it’s a plastic material suitable for the production of components subjected to high temperatures.
Mechanical Properties | |
---|---|
Maximum dimensions | 380mm x 330mm x 300mm |
Ultimate Tensile Strenght | 50 MPa |
Tensile Modulus | 4500 MPa |
Flexural Modulus | 3200 MPa |
Elongation at Break | 5% |
Heat Deflection Temperature | 185° |
Density | 1,3 g/cm3 |
PA12 White
Standard Nylon 12, proposed in different colours: white, grey or black. It’s the ideal solution if you want to check your design or the geometry of a part, in an economical and light way. The material could be reworked, smoothed and painted and has also biocompatibility properties. It’s really a material with multiple uses.
Mechanical Properties | |
---|---|
Maximum dimensions | 380mm x 330mm x 300mm |
Ultimate Tensile Strenght | 50 MPa |
Tensile Modulus | 4500 MPa |
Flexural Modulus | 3200 MPa |
Elongation at Break | 5% |
Heat Deflection Temperature | 185° |
Density | 1,3 g/cm3 |

HP Multi Jet Fusion Material
The professional 3D printing technology HP Multijet Fusion owns several innovations among other 3d printing technologies. The HP 3D printer deposit the material like the inkjet typographic printers. In a very fast way a reagent is sprayed and solidify layer by layer , at high temperature, similar to the melting material’s one. HP Multijet Fusion allows very rapid 3D print of objects in series.
Minimum buildable thickness:0,8mm
Average surface roughness:5/6 µ
Accuracy (part dimension ≤ 150mm):±0,3mm
Accuracy (part dimension > 150mm):±0,05mm ogni 25mm
PA12
Standard Nylon 12 proposed in 2 colours, grey or black. It’s the ideal solution if you want to check your design or the geometry of a part, in an economical and light way. The material could be reworked, smoothed and painted and has also biocompatibility properties. It’s really a material with multiple uses.
Mechanical Properties | |
---|---|
Maximum dimensions | 380mm x 330mm x 300mm |
Ultimate Tensile Strenght | 50 MPa |
Tensile Modulus | 4500 MPa |
Flexural Modulus | 3200 MPa |
Elongation at Break | 5% |
Heat Deflection Temperature | 185° |
Density | 1,3 g/cm3 |